The Effect of Variation of Aluminum Thickness Series 7075 in Heat Treatment Solution on Tensile Strength and Microstructure

This research was conducted to examine the comparison of tensile strength and microstructure between two different aluminum heat treatments. This study aims to compare the microstructure and tensile strength of aluminum 7075 specimens after undergoing solution heat treatment at a temperature of 495°C with soaking time for 30 minutes and experiencing quenching cooling and those without solution heat treatment. The data collection process was carried out by conducting tensile testing and microstructural testing with two specimens each. The test results will be analyzed using tensile strength data and visual microstructure analysis. From the results of the analysis of tensile and microstructural test data, it can be concluded that only the 7075 aluminum specimen with a thickness of 1.4 mm shows the greatest decrease in tensile strength and spread of Mg-Zn and Fe-Al particles, when compared to specimen 7075 with a thickness of 0.6 mm which on the other hand, undergo the separation of Mg-Zn and Fe-Al particles. Meanwhile, the Al 7075 specimen with a thickness of 2.5 mm, the changes that occur only in the diffusion of Mg-Zn particles, which have a slight spread, appear a little faint.