PENGARUH VARIASI LEBAR DAN TEBAL SAYATAN SERAT BAMBU TERHADAP KEKUATAN MEKANIK KOMPOSIT POLYESTER

SISMOYOSARI, SISMOYOSARI (2007) PENGARUH VARIASI LEBAR DAN TEBAL SAYATAN SERAT BAMBU TERHADAP KEKUATAN MEKANIK KOMPOSIT POLYESTER. Other thesis, University of Muhammadiyah Malang.

[img]
Preview
Text
PENGARUH_VARIASI_LEBAR_DAN_TEBAL_SAYATAN_SERAT_BAMBU_TERHADAP_KEKUATAN_MEKANIK_KOMPOSIT_POLYESTER.pdf

Download (51kB) | Preview

Abstract

Composite is merger of lasing and matrik. Orientation, size measure and form of lasing very is influencing is nature of mechanic from is composite. With thick and wide variation of bamboo fibre expected will be got by the nature of maximal mechanic to be is composite Intention of usage of this bamboo fibre beside is easy to got by bamboo have excellence in remarkable resilience and growth. Wide variation of bamboo fibre is 2mm,4mm, and 6mm; for thick variation of 0.6mm,0.8mm and 1mm. Polyester the used is Yukalac QTN polyester 835 / 83K. This composite Examination method use interesting test. Pursuant to result of attempt at wide 2mm thickly 1mm got by biggest interesting strength, while on the contrary to be wide 6mm thickly 0.6mm got by interesting strength which is small. wide got conclusion smaller fibre and thick ever greater of fibre hence interesting strength will growing larger.

Item Type: Thesis (Other)
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Engineering > Department of Mechanical Engineering
Depositing User: Rayi Tegar Pamungkas
Date Deposited: 23 Jun 2012 05:21
Last Modified: 23 Jun 2012 05:21
URI: http://eprints.umm.ac.id/id/eprint/9236

Actions (login required)

View Item View Item