STRESS RELIEF ANNEALING PADA HASIL PENGELASAN (SAW) BAJA API 5L X-52 TERHADAP LAJU RAMBAT RETAKFATIK DAN STRUKTUR MIKRO

MISKAT, IMAM (2008) STRESS RELIEF ANNEALING PADA HASIL PENGELASAN (SAW) BAJA API 5L X-52 TERHADAP LAJU RAMBAT RETAKFATIK DAN STRUKTUR MIKRO. Other thesis, University of Muhammadiyah Malang.

[img]
Preview
Text
STRESS_RELIEF_ANNEALING_PADA_HASIL_PENGELASAN.pdf

Download (52kB) | Preview

Abstract

Fire Steel 5L X-52 is pipe which is made and produced based on standart API that is American Petroleum Institute which this pipe has carbon grade 0,3 % ( journal data Iscor Flat Steel) that is included in medium carbon steel. Problems that is often happened at result of welder SAW ( Submerged Arc Welding) at fire steel 5L-X52 among others is incidence of residual stress and the forming of microstructure in the form ( martensite, retained austenite and carbide) what can reduce ductility or toughness so that doesn't fulfill standart API (American Petroleum Institute). To overcome this problem heat treatment influence stress relief would good for increasing toughness of weld and endurance to speed of propagation of phatic crack at pipe connection of fire steel spiral 5L X-52. Purpose of performed a by this research is aim to improve;repair endurance of speed of propagation of phatic crack at result of welder ( SAW) with treatment of stress relief annealing. From result of research is obtained by conclusion for heat treatment with temperature 5500C, 6500C, 7500C at district Las that for weld metal from steel API 5L X-52 is gotten by propagation of best phatic crack at temperature 5500C with propagator value (ai) 2/10 mm and at cycle (ni) 65155 at temperature 6500C with propagator value (ai) 1,5/10 mm and at cycle (ni) 61547 at temperature 7500C with propagator value (ai) 6,5/10 mm and at cycle (ni) 46633

Item Type: Thesis (Other)
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Faculty of Engineering > Department of Mechanical Engineering
Depositing User: Anggit Aldila
Date Deposited: 15 May 2012 08:13
Last Modified: 15 May 2012 08:13
URI: http://eprints.umm.ac.id/id/eprint/5372

Actions (login required)

View Item View Item