DWI PUTRO, ARIFIAN BAYU (2009) Pengaruh Variasi Kandungan Mn Pada filler dan Variasi Temperatur Untuk Hasil Pengelasan SAW (Submerged Arc Welding) Terhadap Ketangguhan Impact Pada Baja API 5LX60. Other thesis, University of Muhammadiyah Malang.
Pengaruh_Variasi_Kandungan_Mn_Pada_filler_dan_Variasi_TemperaturUntuk_Hasil_Pengelasan_SAW.pdf - Published Version
Download (68Kb) | Preview
One of many kind of welding which be used to joint and give connection in steel construction is submerged Arch Welding or SAW. The principle of SAW weld use electricity current to result arc thus it may melt filler wire, the something is unique in SAW joint is the fluid of welding steel submerged in flux. The goal of this study is to know influence of different Mn containing to filler to SAW joint to strength impact to welding region and HAZ region of API 5LX60 steel. It is done by giving temperature variation at time to testing. In this study writer use API 5LX60 steel as material, it is caused the steel is produced based on the API (American Petroleum Institute) standard. The API 5lx60 with 5L specification constitute specification which be standard by making convention and distribution from line pipe to oil, water and gas by special using.
|Item Type:||Thesis (Other)|
|Subjects:||T Technology > TJ Mechanical engineering and machinery|
|Divisions:||Faculty of Engineering > Department of Mechanical Engineering|
|Depositing User:||Anwar Jasin|
|Date Deposited:||04 Apr 2012 03:38|
|Last Modified:||04 Apr 2012 03:38|
Actions (login required)